Fiberon™ PA6-CF20

极高的强度和韧性
耐热性极佳

Description

Fiberon™PA6-CF20是一款碳纤维增强的PA6(尼龙6)线材。碳纤维增强显著提高了刚度、强度和耐热性,并具有出色的层间附着力。

 

Fiberon™PA6-CF20与PolyMidePA6-CF配方相同,但Fiberon™PA6-CF20打印出的黑色可能略深。

热变形温度高
卓越的各向同性刚性
尺寸稳定

Characteristics

Printing Temperature:

280˚C - 300˚C

Bed Temperature:

25˚C - 50˚C

Printing Speed:

30mm/s -60mm/s

Fan:

OFF

Direct Drive Retraction Distance:

3mm

Direct Drive Retraction Speed:

40mm/s

Indirect Drive Retraction Distance:

6mm

Indirect Drive Retraction Speed:

60mm

Drying Settings:

100˚C for 8h

Dry Settings Notes:

(Only if the material has absorbed moisture)

Annealing:

80˚C for 6h

Colors

Colors

No SKUs found!

Series

Specifications

Fiberon™ PA6-CF20

print
settings

Printing Temperature:
280˚C - 300˚C
Bed Temperature:
25˚C - 50˚C
Printing Speed:
30mm/s -60mm/s
Fan:
OFF
Direct Drive Retraction Distance:
3mm
Direct Drive Retraction Speed:
40mm/s
Indirect Drive Retraction Distance:
6mm
Indirect Drive Retraction Speed:
60mm
Annealing:
80˚C for 6 h
Dry Settings:
100˚C for 8h
(Only if the material has absorbed moisture)

MEchanical Properties

(XY)Young's Modulus (MPa):
7453.5 ± 656.2 MPa
ISO 527, GB/T 1040
(Z)Young's Modulus (MPa):
4354.5 ± 206.4 MPa
ISO 527, GB/T 1040
(XY)Tensile Strength:
105. ± 5.0 MPa
ISO 527, GB/T 1040
(Z)Tensile Strength:
67.7 ± 4.7 MPa
ISO 527, GB/T 1040
(XY)Elongation at break(%):
3.0 ± 0.3 %
ISO 527, GB/T 1040
(Z)Elongation at break(%)
2.5 ± 0.7 %
ISO 527, GB/T 1040
(XY)Bending Modulus (MPa):
8339.4 ± 369.4 MPa
ISO 178, GB/T 9341
(XY)Bending Strength (MPa):
169.0 ± 4.7 MPa
ISO 178, GB/T 9341
(XY)Charpy Impact Strength:
13.3 ± 0.5 kJ/m2
ISO 179, GB/T 1043

Thermal Properties

Glass Transition Temperature:
74.2 °CPolyMide™ PA6-CF is a 20% carbon fiber reinforced Nylon 6 filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion thanks to Fiber Adhesion™ Technology. PolyMide™ PA6-CF outperforms almost every 3D printing material, offering extreme durability and functionality while featuring a heat deflection temperature of 215°C.
DSC, 10°C/min
Melting Temperature:
74.2 °CPolyMide™ PA6-CF is a 20% carbon fiber reinforced Nylon 6 filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion thanks to Fiber Adhesion™ Technology. PolyMide™ PA6-CF outperforms almost every 3D printing material, offering extreme durability and functionality while featuring a heat deflection temperature of 215°C.
DSC, 10°C/min
Heat Deflection Temperature
(1.8MPa):
173.1 °C
ISO 75 1.8MPa
Heat Deflection Temperature
(0.45MPa)
215.2 °C
ISO 75 0.45MPa

Material Properties

Technology

Warp-Free technology

Fiber adhesion technology

Hello Polymaker

Choose your region:

North America

Please fill in the form below or if you have other questions are not included in the form, please contact us through inquiry.na@polymaker.com.cn. We will get back to you soon.

Europe

Please fill in the form below or if you have other questions are not included in the form, please contact us through sales.eu@polymaker.com.cn. We will get back to you soon.

Rest of the World

Please fill in the form below or if you have other questions are not included in the form, please contact us through contact.ppac@polymaker.com.cn. We will get back to you soon.

chevron-left-circlechevron-right-circle